B级全牙镍基合金螺杆
B-level full-tooth nickel-based alloy screw
加工范围:¢22mm-¢300mm
Processing range: ¢ 22mm-¢ 300mm
原料母材:SKD11、42CMO
Raw base material: SKD11,42CMO
材料调制时间:48小时,调质硬度HRC30℃
Modulation hardness of HRC30°C for 48 hours
合金硬度:HRC62-65℃左右
alloy hardness: about 62-65°C in HRC
合金成份:Fe+Ni+Cu+Mo+Cr(镍基合金粉末)
Alloy composition: Fe + Ni + Cu + Mo + Cr (nickel-based alloypowder)
合金层厚度:0.8-2.5
thickness of alloy layer is 0.8 - 2.5
螺杆直线度:0.015mm/m
Screw straightness: 0.015mm / m
表面光洁度:Ra0.6um
Surface finish: Ra0.6um
适用于生产塑胶类:腐蚀性大、磨损大含玻纤量为25%-45%,LCP、PA、PC、PBT、PP、PET、PA66、PA666、PEK及无卤料(专用).