Vectra?LCP:
Vectra?LCP: A115,A130,A140,A150,A150B,A150F,A230,A330S,A410,A422,A430,A435,A460, A466,A470,A540,A625,A700,A725,A950,B130,B230,C130,C130M,C140,C150,C400, C810,C820,D130M,E130,E130G,E130i,E140i,E150i,E463i,E471i,E472i,E473i,E480i, E488i,E540i,E820i,E820iPd,MT1300,MT1305,MT1310,MT1335,MT4310,MT4350,S135, S140M,S150,S471,S475,SG02C,SG03C,SG52C,T130,T130M,T150,V140,V143XL,V400P.
A115,Provides easier flow than A130.Slightly tougher, but may warp slightly more than A130 in some parts.15%glassreinforced.
A130:The Standard for the Industry. Excellent balance of properties, including easy flow, easy processing, thermalstability, chemical resistance, mechanical and electrical properties. Suitable for vapor phase surface mountelectrical and electronic devices. 30% glass reinforced
A140:Improved creep resistance over A130. May reduce warpage in some parts compared to A130. 50% glassreinforced. Chemical abbreviation according to ISO 1043-1 : LCP Inherently flame retardant FDA compliant ULListingV-0 in natural and black at 0.45mm thickness per UL 94 flame testing, and UL-5VA in natural at 1.5mm.Relative-Temperature-Index (RTI) according to UL 746B: electrical 220°C, mechanical 220°C at 0.8mm. UL =Underwriters Laboratories (USA)
A150:Improved creep resistance over A130. May reduce warpage in some parts compared to A130. 50% glassreinforced. Chemical abbreviation according to ISO 1043-1 : LCP Inherently flame retardant FDA compliant ULListingV-0 in natural and black at 0.45mm thickness per UL 94 flame testing, and UL-5VA in natural at 1.5mm.Relative-Temperature-Index (RTI) according to UL 746B: electrical 220°C, mechanical 220°C at 0.8mm. UL =Underwriters Laboratories (USA)
A150B:50%Glass beads filled, Low anisotropy
A150F:50%Glass flakes filled, Low warpage
A230, Exceptional stiffness.Electrically conductive. 30% carbon fiber reinforced.
A330S,
A410,:Lowwarpage,High stiffness 50%GF/M
A422:Glass/Graphite Filled
A430, Provides many of the characteristics of A130 with added lubricity. Suitable for applications requiring excellent
wear characteristics. Excellent electrical properties at high frequencies.LCP/PTFE blend.
A435, Similar to A430 with added stiffness. Best High Current Arc Ignition (HAI) performance. Glass/PTFE filled.
A460,50%Glass beads filled, Low anisotropy
A466,
A470, Low warpage,High stiffness 50%
A540,40% Mineral Filled
A625:25% Graphite Filled
A700:30% Glass Reinforced
A725, Conductive grade, smooth surface compared to A700. 25 % filled
A950:Base resin having a melt point of 280°C.Suitable for extrusion into film, sheet, and fibers. Not recommended for injection molding
B130: 30% Glass Reinforced
B230,30% Carbon Fiber Reinforced
C130,30% Glass Reinforced
C130M,
C140,
C150,50% Glass Reinforced
C400, Mineral reinforced, Plateable Heat Resistant
C810, Many of the characteristics of C130.Suitable for electroplating for line widths down to 10 mils. Glass/mineral filled
典型的用途：用于制造各种零件，可用于电气/电子、照明、电讯、汽车点火和燃料处理、宇航、光纤、电动机、成像装置、传感器、烘箱器皿、燃料或气体阻挡结构等。